| Bottle Top Mold | (english) Ingot mold, with the top constricted; used in the manufacture of capped steel, the metal in the constriction being covered with a cap fitting into the bottle-neck, which stops rimming action by trapping escaping gases. |
| Box Annealing | (english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. |
| Box Annealing 2 | (english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
| Brale | (english) A diamond penetrator, conical in shape, used with a Rockwell hardness tester for hard metals. |
| Braze Welding | (english) A family of welding procedures where metals are joined by filler metal that has a melting temperature below the solidus of the parent metal, but above 840 (450 C). |
| Brazing | (english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet. |
| Break Test (for tempered steel) | (english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges. |
| Bridling | (english) The cold working of dead soft annealed strip metal immediately prior to a forming, bending, or drawing operation. A process designed to prevent the formulation of Luder's lines. Caution-Bridled metal should be used promptly and not permitted to (of itself) return to its pre-bridled condition. |
| Brinell Hardness | (english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested. |
| Brinell Hardness Number | (english) The value of hardness of a metal on an arbitrary scale representing kg/mm2, determined by measuring the diameter of the impression made by a ball of given diameter applied under a known load. Values are expressed in Brinell Hardness Numbers, BHN |