Blue Brittleness 2 |
(english) Reduced ductility occurring as a result of strain aging, when certain ferrous alloys are worked between 300 and 700 (degrees) F. This phenomenon may be observed at the working temperature or subsequently at lower temperatures. |
Blush |
(english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive. |
Body-Centered |
(english) Having the equivalent lattice points at the corners of the unit cell, and at its center; sometimes called centered, or space-centered. |
Boil |
(english) Agitation of a bath of metal caused by the liberation of a gas beneath its surface. May be deliberately induced by the addition of oxidizing material to a bath containing excess carbon. In the later case it is called a carbon boil and CO or CO2 are liberated. |
Boiler |
(english) A closed vessel in which water, is transformed into steam at a given pressure and temperature under controlled conditions. |
Boron (chemical symbol B) |
(english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration. |
Bottom Roll |
(english) Submerged roll in the pot used to keep the strip submerged in the pot. |
Box Annealing |
(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. |
Box Annealing 2 |
(english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
Brake |
(english) A piece of equipment used for bending sheet; also called a bar folder. If operated manually, it is called a hand brake; if power driven, it is called a press brake. |