| Blasting (Blast Cleaning) | (english) A process for cleaning or finishing metal objects by use of an air blast or centrifugal wheel that throws abrasive particles against the surface of the work pieces. Small, irregular particles of steel or iron are used as the abrasive in grit blasting, and steel or iron balls in shot blasting. |
| BLEED-OFF | (english) To divert a specific, controllable portion of pump delivery directly to reservoir. |
| Blister | (english) 1) Coating defect consisting of the formation of bubbles in a coating, which appear as hemispherical elevations. The blisters are hollow, and are usually caused by entrapped air or solvent. 2) A raised spot on the surface on the surface of metal due to expansion of gas which causes a subsurface metal separation such as inclusions and small laminations. |
| Blister 2 | (english) A defect in metal, on or near the surface, resulting from the expansion of gas in a subsurface zone. Very small blisters are called pinheads or pepper blisters. |
| Blister Steel | (english) High-carbon steel produced by carburizing wrought iron. The bar, originally smooth, is covered with small blisters when removed from the cementation (carburizing) furnace. |
| Bloom 2 | (english) A semi-finished hot rolled product, rectangular in cross section, produced on a blooming mill. For iron and steel, the width is not more than twice the thickness, and the cross-sectional area is usually not less than 36 sq. in. Iron and steel blooms are sometimes made by forging. |
| Blooming-Mill | (english) A mill used to reduce ingots to blooms, billets slabs, sheet-bar etc., |
| Blow Back | (english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film. |
| Blue Annealing | (english) Heating hot rolled ferrous sheet in an open furnace to a temperature within the transformation range and then cooling in air, in order to soften the metal. The formation of a bluish oxide on the surface is incidental. |
| Blue Brittleness | (english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. |