| Base Type | (english) Tin Mill term; Thickness divided by .00011. Also weight in pounds of one Base Box of Tin plate. In finished inventory base weight is specified instead of decimal thickness. |
| Basket Screen | (english) A first stage in-line water filter for water delivered from the New Blowing Room Pump Room to the Blast Furnace. The strainer contains an electric-driven rotary sieve that catches particulates and prevents them from entering the water system. |
| Blister | (english) 1) Coating defect consisting of the formation of bubbles in a coating, which appear as hemispherical elevations. The blisters are hollow, and are usually caused by entrapped air or solvent. 2) A raised spot on the surface on the surface of metal due to expansion of gas which causes a subsurface metal separation such as inclusions and small laminations. |
| Blow Back | (english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film. |
| Bridling | (english) The cold working of dead soft annealed strip metal immediately prior to a forming, bending, or drawing operation. A process designed to prevent the formulation of Luder's lines. Caution-Bridled metal should be used promptly and not permitted to (of itself) return to its pre-bridled condition. |
| Bright Annealing 2 | (english) The process of annealing in a protective atmosphere so as to prevent discoloration of the bright surface desired. |
| Closure | (Environmental Engineering) The act of preparing a landfill for long term inactivity, including placement of a cover over the landfill to prevent infiltration of surface water. |
| Global warming | (Environmental Engineering) The long-term warming of the plant due to increases in greenhouse gases which trap reflected light preventing it from exiting to space. |
| Runoff | (Environmental Engineering) The water that flows overland to lakes or streams during and shortly after a precipitation event. |
| Carbonation | (Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%. |