| Blue Brittleness 2 | (english) Reduced ductility occurring as a result of strain aging, when certain ferrous alloys are worked between 300 and 700 (degrees) F. This phenomenon may be observed at the working temperature or subsequently at lower temperatures. |
| Blush | (english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive. |
| Boiler | (english) A closed vessel in which water, is transformed into steam at a given pressure and temperature under controlled conditions. |
| Bonderizing | (english) The coating of steel with a film composed largely of zinc phosphate in order to develop a better bonding surface for paint or lacquer. |
| Bottle Top Mold | (english) Ingot mold, with the top constricted; used in the manufacture of capped steel, the metal in the constriction being covered with a cap fitting into the bottle-neck, which stops rimming action by trapping escaping gases. |
| Bottom Up | (english) Reversing the wrap of a coil putting the top surface on the bottom. |
| Box Annealing | (english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. |
| Box Annealing 2 | (english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
| Brake | (english) A piece of equipment used for bending sheet; also called a bar folder. If operated manually, it is called a hand brake; if power driven, it is called a press brake. |
| Brass | (english) An alloy that is 70% copper,30% zinc. One of the most widely used of the copper-zinc alloys; malleable and ductile; excellent cold-working but poor hot-working and machining properties; excellent for soft-soldering; good for silver alloy brazing or oxyacetylene welding, but fair for resistance or carbon-arc welding. Used for drawn cartridges, tubes, eyelets machine items and snap fasteners. |