| Calcium Aluminate Cement |
(Concrete Engineering) The product obtained by pulverizing clinker consisting essentially of hydraulic calcium aluminates resulting from fusing or sintering a suitable proportioned mixture of aluminous and calcareous materials. |
| Carbonation |
(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%. |
| HRM High Reactivity Metakaolin. |
(Concrete Engineering) Refined form of an ASTM C618, Class N (natural) pozzolan. A high performance, mineral admixture, similar in performance to silica fume, additionally comparable in cost. Pure white powdered in form will, not effect the natural color or darken concrete as silica fume does. Suitable for high-performance color matching in architectural concrete. Dosage at 5% to 10%, of cement by weight. No bleed water, better finishability, more creamy, cleanup is easier with slightly higher 28 day strengths and 25% - 35% less plasticizer is required than silica fume. |
| Hydrogenesis |
(Concrete Engineering) Another term for condensation. The term is especially applied to base and soil substrates under highway pavements. where the barometric pump causes the inhalation of humid air, which then condenses in those structures, causing an ever increasing moisture content and sometimes instability. |
| Screen (or Sieve) |
(Concrete Engineering) A metallic sheet or plate, woven wire cloth, or similar device, with regularly spaced openings of uniform size, mounted in a suitable frame or holder for use in separating material according to size. |
| adjustable parallels |
แท่งโลหะหรือไม้รูปลิ่มสองแท่ง สำหรับจัดแต่ระยะให้เพิ่มขึ้นหรือลดลง |
| adjustable reamer |
เครื่องคว้านรู ที่ปรับขนาดให้กว้างหรือแคบลงได้ |
| adjustable shelves |
ชั้นหรือหิ้งที่ปรับระยะขึ้นลงได้ |
| butterfly table |
โต๊ะกลมหรือโต๊ะเหลี่ยมของพวกอเมริกันในต้นศตวรรษที่ 17 เริ่มมีใช้กันในรัฐคอนเนคติกัตเป็นแห่งแรก หน้าโต๊ะพับลงได้ทั้ง 2 ข้างเวลาใช้งานก็พลิกหน้าโต๊ะขึ้น รองรับด้วยค้ำยันทั้ง 2 ข้าง ลักษณะเป็นปีกผีเสื้อ ส่วนขาทั้งสี่เป็นไม้กลึง ปลายขาถ่างออกจากกัน อาจมีลิ้นชักที่หัวโต๊ะทั้ง 2 ด้าน
|
| bag table |
โต๊ะเล็ก ๆ ใช้กันในศตวรรษที่ 18 มีลักษณะเหมือนโต๊ะลิ้นชักแต่แขวนถุงผ้าติดถ้อยไว้กับโต๊ะ ใช้เก็บของ |