| Aging 1 |
(english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging. |
| Aging 2 |
(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures. |
| ภาคีวิศวกรสาขาอุตสาหการ |
Associate Industrial Engineer
|
| BACK PRESSURE |
(english) The level of pressure on the return or downstream side of a device or system. |
| Backwardation |
(english) Market condition where the spot, or current price for a metal is higher than the three-month delivery price. This usually indicates immediate demand is perceived to be stronger than long-term demand. Not considered to be a "normal" market state (See Contango). |
| Bainite |
(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite. |
| Bake Hardenable Steel |
(english) A cold-rolled, low-carbon sheet steel used for automotive body panel applications. Because of the steel’s special processing, it has good stamping and strength characteristics and after paint is baked on, improved dent resistance. |
| Baked Strength |
(english) Compressive, shear, tensile or transverse strength of a mold sand mixture when baked at a temperature above 231 B0F (111 B0C) and then cooled to room temperature. |
| Balanced Steel |
(english) Steels in which the deoxidisation is controlled to produce an intermediate structure between a rimmed and killed steel, Sometimes referred to as semi-killed steels, they possess uniform properties throughout the ingot and amongst their applications are boiler plate and structural sections. |
| Bamboo Grain Structure |
(english) A structure in wire or sheet in which the boundaries of the grains tend to be aligned normal to the long axis and to extend completely through the thickness. |