| A Sheet Metal Screw | (english) Sheet metal screws with (a) sharp-pointed ends; and (b) fewer threads per inch than type AB screws; and (c) deeper threads with bettere gripping power than type AB. The industrial Fasteners Institue incorrectly labes type A an “obsolete” thread though it is universally preferred in 18-8 stainless over type AB, especially by the marine industry. |
| Addition Agent | (english) 1) Any material added to a charge of molten metal in bath or ladle to bring alloy to specifications, 2) reagent added to plating bath. |
| Bake Hardenable Steel | (english) A cold-rolled, low-carbon sheet steel used for automotive body panel applications. Because of the steel’s special processing, it has good stamping and strength characteristics and after paint is baked on, improved dent resistance. |
| Band Saw Steel (Wood) | (english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45. |
| Base Type | (english) Tin Mill term; Thickness divided by .00011. Also weight in pounds of one Base Box of Tin plate. In finished inventory base weight is specified instead of decimal thickness. |
| Batch Anneal | (english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal. |
| Bend Test | (english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested. |
| Blanking | (english) An early step in preparing flat-rolled steel for use by an end user. A blank is a section of sheet that has the same outer dimensions as a specified part (such as a car door or hood) but that has not yet been stamped. Steel processors may offer blanking for their customers to reduce their labor and transportation costs; excess steel can be trimmed prior to shipment. |
| BLEED-OFF | (english) To divert a specific, controllable portion of pump delivery directly to reservoir. |
| Blue Brittleness | (english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. |