| Bainite | (english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite. |
| Band Saw Steel (Wood) | (english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45. |
| Band Wareroom | (english) A storage area in Strip Steel used for storing hot bands (coil made from slab). |
| Base | (english) The steel or concrete pedestal on which the coils are stacked during the batch annealing process. |
| Base Metal | (english) (1) The metal present in the largest proportion in an alloy; (2) the metal to be brazed, cut or welded; (3) after welding the part of the metal that was not melted during the process. |
| Basket Screen | (english) A first stage in-line water filter for water delivered from the New Blowing Room Pump Room to the Blast Furnace. The strainer contains an electric-driven rotary sieve that catches particulates and prevents them from entering the water system. |
| Bearing Load | (english) A compressive load supported by a member, usually a tube or collar, along a line where contact is made with a pin, rivet, axle, or shaft. |
| Bearing Strength | (english) The maximum bearing load at failure divided by the effective bearing area. In a pinned or riveted joint, the iffective area is calculated as the product of the diameter of the hole and the thickness of the bearing member. |
| Bell Mouth | (english) The flaring or tapering of a machined hole, usually made at the entrance end because of misalignment or spring of the cutting tool. |
| Bend Test | (english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested. |