| internal stress resultant | หน่วยแรงรับภายใน |
| resultant force | แรงลัพธ์ |
| Acid Brittleness (Pickling Brittleness) | (english) Brittleness resulting from pickling steel in acid; hydrogen, formed by the interaction between iron and acid, is partially absorbed by the metal, causing acid brittleness. |
| Acid-Brittleness | (english) Brittleness resulting from pickling steel in acid; hydrogen, formed by the interaction between iron and acid, is partially absorbed by the metal, causing acid brittleness. |
| Bend Test | (english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested. |
| Blister 2 | (english) A defect in metal, on or near the surface, resulting from the expansion of gas in a subsurface zone. Very small blisters are called pinheads or pepper blisters. |
| Blue Brittleness 2 | (english) Reduced ductility occurring as a result of strain aging, when certain ferrous alloys are worked between 300 and 700 (degrees) F. This phenomenon may be observed at the working temperature or subsequently at lower temperatures. |
| Blush | (english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive. |
| Breakout | (english) An accident caused by the failure of the walls of the hearth of the furnace resulting in liquid iron or slag (or both) flowing uncontrolled out of the blast furnace. |
| Brinell Hardness Testing | (english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function. |