| Boil | (english) Agitation of a bath of metal caused by the liberation of a gas beneath its surface. May be deliberately induced by the addition of oxidizing material to a bath containing excess carbon. In the later case it is called a carbon boil and CO or CO2 are liberated. |
| Bonding Clay (Bonderise) | (english) Any clay suitable for use as a bonding material. |
| Box Annealing 2 | (english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
| Brazing | (english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet. |
| Brinell Hardness | (english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested. |
| Brinell Hardness Test | (english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula. |
| Brinell Hardness Testing | (english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function. |
| Brittleness | (english) The tendency of a metal or material to fracture without undergoing appreciable plastic deformation. |
| Builtup Plate | (english) "A pattern plate of suitable material, with the cope pattern mounted on or attached to one side; the drag pattern may be attached to the other side or to a separate mounting. See Matchplate " |
| Burn-Out | (english) Firing a mold at a high temperature to remove pattern material residue. |