| workability | ความสามรถเทได้ |
| Age Hardening | (english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures. |
| Agglomerating Processes | (english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces. |
| Aging 1 | (english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging. |
| AIR BLEEDER AUTOMATIC | (english) A valve that is fit into a hydraulic pipeline to facilitate automatic release of air trapped in the pipeline. See also AIR BLEEDER, MANUAL. |
| Bainite | (english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite. |
| Basic Oxygen Process 2 | (english) A steel making process wherein oxygen of the highest purity is blown onto the surface of a bath of molten iron contained in a basic lined and ladle shaped vessel. The melting cycle duration is extremely short with quality comparable to Open Hearth Steel. |
| Bend Test | (english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested. |
| BLADDER | (english) A separator or diaphragm usually found in a chamber to facilitate separation of two (2) fluids or gases. |
| Blow Back | (english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film. |