| Blush | (english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive. |
| Boil | (english) Agitation of a bath of metal caused by the liberation of a gas beneath its surface. May be deliberately induced by the addition of oxidizing material to a bath containing excess carbon. In the later case it is called a carbon boil and CO or CO2 are liberated. |
| Bonderized Coating | (english) A thin film of phosphate pretreatment applied to a steel surface (bare or zinc coated) to enhance paintability. |
| Bonderizing | (english) The coating of steel with a film composed largely of zinc phosphate in order to develop a better bonding surface for paint or lacquer. |
| Boron (chemical symbol B) | (english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration. |
| Box Annealing | (english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. |
| Box Annealing 2 | (english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
| Brass | (english) An alloy that is 70% copper,30% zinc. One of the most widely used of the copper-zinc alloys; malleable and ductile; excellent cold-working but poor hot-working and machining properties; excellent for soft-soldering; good for silver alloy brazing or oxyacetylene welding, but fair for resistance or carbon-arc welding. Used for drawn cartridges, tubes, eyelets machine items and snap fasteners. |
| Brasses | (english) Copper base alloys in which zinc is the principal alloying element. Brass is harder and mechanically stronger than either of its alloying elements copper or zinc. It is formable and ductile; develops high tensile strength with cold-working and is not heat treatable. |
| Braze Welding | (english) A family of welding procedures where metals are joined by filler metal that has a melting temperature below the solidus of the parent metal, but above 840 (450 C). |