| Blaine Fineness | (Concrete Engineering) The fineness of granular materials such as cement and pozzolan, expressed as total surface area in square centimeters per gram, determined by the Blaine air-permeability apparatus and procedure. |
| Blast Furnace Slag | (Concrete Engineering) A non-metallic waste product developed in the manufacture of pig iron, consisting basically of a mixture of lime, silica and alumina, the same oxides that make up portland cement, but not in the same proportions or forms. It is used both in the manufacture of portland blast furnace slag cement and as an aggregate for lightweight concrete. |
| Bleeding, Bleed Water | (Concrete Engineering) A form of segregation in which some of the water in a mix tends to rise to the surface of freshly placed concrete. Known also as water gain. |
| Calcium Aluminate Cement | (Concrete Engineering) The product obtained by pulverizing clinker consisting essentially of hydraulic calcium aluminates resulting from fusing or sintering a suitable proportioned mixture of aluminous and calcareous materials. |
| Carbonation | (Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%. |
| Cement, Portland (ASTM C150) (Concrete Engineering) | A powdery substance made by burning, at a high temperature, a mixture of clay and limestone producing lumps called “clinkers” which are ground into a fine powder consisting of hydraulic calcium silicates. For non-portland cements, see aluminous cement. |
| Cement Content | (Concrete Engineering) A quantity of cement contained in a unit volume of concrete or mortar, ordinarily expressed as pounds, barrels, or bags per cubic yard. |
| Cold Joint | (Concrete Engineering) A visible lineation which forms when the placement of concrete is delayed. The concrete in place hardens prior to the next placement of concrete against it. |
| Dispersing Agent | (Concrete Engineering) An admixture capable of increasing the fluidity of pastes, mortars, or concretes by reduction of interparticle attraction. |
| Dry Rodded Weight | (Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container |