| Absorbed Moisture | (Concrete Engineering) Moisture which is mechanically held in a material. In aggregates, that water which is not available to become part of the mixing water is designated "absorbed" water. |
| Adsorption Water | (Concrete Engineering) Water held on surfaces in a material by either physical and/or chemical forces. |
| Bleeding, Bleed Water | (Concrete Engineering) A form of segregation in which some of the water in a mix tends to rise to the surface of freshly placed concrete. Known also as water gain. |
| Carbonation | (Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%. |
| HRM High Reactivity Metakaolin. | (Concrete Engineering) Refined form of an ASTM C618, Class N (natural) pozzolan. A high performance, mineral admixture, similar in performance to silica fume, additionally comparable in cost. Pure white powdered in form will, not effect the natural color or darken concrete as silica fume does. Suitable for high-performance color matching in architectural concrete. Dosage at 5% to 10%, of cement by weight. No bleed water, better finishability, more creamy, cleanup is easier with slightly higher 28 day strengths and 25% - 35% less plasticizer is required than silica fume. |
| Hydrologic Cycle | (Concrete Engineering) The Hydrologic Cycle consists of the evaporation of water from oceans and other bodies of open water; condensation to produce cloud formations; precipitation of rain, snow, sleet or hail upon land surfaces; dissipation of rain or melted solids by direct run-off into lakes and by seepage into the soil. Thereby producing a continuing endless source of water in the sub-grade. |
| Impermeable | (Concrete Engineering) The ability of a material or product to reduce or eliminate gaseous transmissions through it's mass; measured as the rate of Water Vapor Transmission (WVT). Note: Not all materials that are waterproof are vaporproof; all materials that are vaporproof are inherently waterproof. |
| Neat Cement-Paste | (Concrete Engineering) A mixture of water and hydraulic cement, both before and after setting and hardening. |
| Non-evaporable Water | (Concrete Engineering) The water in concrete which is irremovable by oven drying; chemically combined during cement hydration. |
| Pumping (of Pavements) | (Concrete Engineering) The ejection of a mixture of water and solid materials such as clay or silt along cracks, transverse or longitudinal joints, and along pavement edges caused by downward slab movement due to the passage of heavy loads, machinery or equipment over the pavement after free water has accumulated in or on the subbase, subgrade or basecourse. |