| Basic Oxygen Furnace (BOF) | (english) "WHAT A pear-shaped furnace, lined with refractory bricks, that refines molten iron from the blast furnace and scrap into steel. Up to 30% of the charge into the BOF can be scrap, with hot metal accounting for the rest. WHY BOFs, which can refine a heat (batch) of steel in less than 45 minutes, replaced open-hearth furnaces in the 1950s; the latter required five to six hours to process the metal. The BOF's rapid operation, lower cost and ease of control give it a distinct advantage over previous methods. HOW Scrap is dumped into the furnace vessel, followed by the hot metal from the blast furnace. A lance is lowered from above, through which blows a high-pressure stream of oxygen to cause chemical reactions that separate impurities as fumes or slag. Once refined, the liquid steel and slag are poured into separate containers. " |
| Bazooka | (english) Performs functions of Galvanneal Furnace; set of torches on wheels used to shoot flames onto a strip to further heat it. |
| Bench-Blower | (english) A small core-blowing machine, utilizing a removable sand magazine and blow heat. |
| Bend Test | (english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested. |
| Bent Axis Pumps | (english) In this pump, the pistons are at an angle to the drive shaft and Thrust Plate. The piston block shaft is connected to the drive shaft by a universal joint, not shown. The drive shaft, thrust plate, piston block shaft, and piston block all revolve. The connecting rods are attached to the thrust plate and revolve with it, unlike the swash plate pump where the piston rods slide past a stationary swash plate. The outlet ports are semi-circular holes in the Valve Plate, shown on the far right of the animation on edge and in a head-on view below, right. As the pump revolves, half the pistons suck in fluid as they pass over the intake port. The other pistons discharge their fluid through the outlet port. This pump should be compared to the radial piston pump, swash plate pump, and wobble pump. |
| Billet 2 | (english) A solid semi-finished round or square product that has been hot worked by forging, rolling, or extrusion. An iron or steel billet has a minimum width or thickness of 1 1/2 in. and the cross-sectional area varies from 2 1/4 to 36 sq. in. For nonferrous metals, it may also be a casting suitable for finished or semi-finished rolling or for extrusion. |
| Blast Furnace 2 | (english) A vertical shaft type smelting furnace in which an air blast is used, usually hot, for producing pih iron. The furnace is continuous in operation using iron ore, coke, and limestone as raw materials which are charged at the top while the molten iron and slag are collected at the bottom and are tapped out at intervals. |
| Blister | (english) 1) Coating defect consisting of the formation of bubbles in a coating, which appear as hemispherical elevations. The blisters are hollow, and are usually caused by entrapped air or solvent. 2) A raised spot on the surface on the surface of metal due to expansion of gas which causes a subsurface metal separation such as inclusions and small laminations. |
| Blow Back | (english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film. |
| Blue Brittleness | (english) Brittleness exhibited by some steels after being heated to some temperature within the range of 300 (degrees) to 650 (degrees) F, and more especially if the steel is worked at the elevated temperature. Killed steels are virtually free of this kind of brittleness. |