| Calcine | (Concrete Engineering) To alter composition or physical state by heating to a specific temperature for a specific length of time. |
| Calcium Aluminate Cement | (Concrete Engineering) The product obtained by pulverizing clinker consisting essentially of hydraulic calcium aluminates resulting from fusing or sintering a suitable proportioned mixture of aluminous and calcareous materials. |
| Carbonation | (Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%. |
| Cellular Concrete | (Concrete Engineering) A lightweight product consisting of portland cement, cement-pozzolan, cement sand, lime-pozzolan, or lime-sand pastes, or pastes containing blends of these ingredients and having a homogenous void or cell structure, attained with gas forming chemicals or foaming agents. For cellular concretes, containing binder ingredients other than or in addition to portland cement, autoclave curing is usually employed. |
| Cement, Portland (ASTM C150) (Concrete Engineering) | A powdery substance made by burning, at a high temperature, a mixture of clay and limestone producing lumps called “clinkers” which are ground into a fine powder consisting of hydraulic calcium silicates. For non-portland cements, see aluminous cement. |
| Cold Joint | (Concrete Engineering) A visible lineation which forms when the placement of concrete is delayed. The concrete in place hardens prior to the next placement of concrete against it. |
| Consistency | (Concrete Engineering) The degree of plasticity of fresh concrete or mortar The normal measure of consistency is slump for concrete and flow for mortar. |
| Dispersing Agent | (Concrete Engineering) An admixture capable of increasing the fluidity of pastes, mortars, or concretes by reduction of interparticle attraction. |
| Elastic Shortening | (Concrete Engineering) The shortening of a member in pre-stressed concrete which occurs on the application of forces induced by prestressing. |
| Entrained Air (See air entrainment) | (Concrete Engineering) Microscopic air bubbles intentionally incorporated in mortar or concrete, to improve workability and durability (usually imparting a higher degree of resistance to freezing and thawing). |