| Agglomerating Processes | (english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces. |
| Aging 1 | (english) A change in the properties of certain metal and alloys (such as steel) that occurs at ambient or moderately elevated temperatures after a hot working heat treatment or cold working operation. Typical properties impacted are hardness, yield strength, tensile strength, ductility, impact value, formability, magnetic properties, etc. See also Non-aging. |
| Aging 2 | (english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures. |
| ใบอนุญาตเป็นผู้ประกอบวิชาชีพวิศวกรรมควบคุม | Licence for Professional Practice (วสท.) - or Controlled Engineer License , Registed Engineer License |
| Back End | (english) 1) Usually refers to the entry end of process lines. 2) The outside lap 2) of the produced coil, or the inside lap of the consumed coil. |
| Backer (back-up plate) | (english) A “tool” or reinforcing part, which presses against the outer surface of an extrusion die, supporting it against the pressure of the extruding metal. The backer has an opening larger than the die aperture, allowing the extruded product to emerge without marring its soft surface. |
| Backoff | Removal of part of coil from entry end of unit; may be necessitated by a defect in coil or by a wreck in the mill, etc. Backoff weight is the part of the coil that is removed and not finished/produced. |
| Bainite | (english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite. |
| Bake Hardenable Steel | (english) A cold-rolled, low-carbon sheet steel used for automotive body panel applications. Because of the steel’s special processing, it has good stamping and strength characteristics and after paint is baked on, improved dent resistance. |
| Baked Core | (english) A core which has been heated through sufficient time and temperature to produce the desired physical properties attainable from its oxidizing or thermal-setting binders. |