| Boiler | (english) A closed vessel in which water, is transformed into steam at a given pressure and temperature under controlled conditions. |
| Boron (chemical symbol B) | (english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration. |
| Bottle Top Mold | (english) Ingot mold, with the top constricted; used in the manufacture of capped steel, the metal in the constriction being covered with a cap fitting into the bottle-neck, which stops rimming action by trapping escaping gases. |
| Box Annealing | (english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. |
| Box Annealing 2 | (english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
| Brake | (english) A piece of equipment used for bending sheet; also called a bar folder. If operated manually, it is called a hand brake; if power driven, it is called a press brake. |
| Brake Press Bending | (english) An operation which produces various degree bends when fabricating parts from steel. |
| Brale | (english) A diamond penetrator, conical in shape, used with a Rockwell hardness tester for hard metals. |
| Brass | (english) An alloy that is 70% copper,30% zinc. One of the most widely used of the copper-zinc alloys; malleable and ductile; excellent cold-working but poor hot-working and machining properties; excellent for soft-soldering; good for silver alloy brazing or oxyacetylene welding, but fair for resistance or carbon-arc welding. Used for drawn cartridges, tubes, eyelets machine items and snap fasteners. |
| Brasses | (english) Copper base alloys in which zinc is the principal alloying element. Brass is harder and mechanically stronger than either of its alloying elements copper or zinc. It is formable and ductile; develops high tensile strength with cold-working and is not heat treatable. |