| Boil | (english) Agitation of a bath of metal caused by the liberation of a gas beneath its surface. May be deliberately induced by the addition of oxidizing material to a bath containing excess carbon. In the later case it is called a carbon boil and CO or CO2 are liberated. |
| Boiler | (english) A closed vessel in which water, is transformed into steam at a given pressure and temperature under controlled conditions. |
| Box Annealing | (english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing. |
| Box Annealing 2 | (english) A process of annealing a ferrous alloy in a closed metal container, with or without packing materials, in order to minimize the effects of oxidation. The charge is normally heated slowly to a temperature below the transformation range, but occasionally above or within it, and then is slowly cooled. |
| Brake | (english) A piece of equipment used for bending sheet; also called a bar folder. If operated manually, it is called a hand brake; if power driven, it is called a press brake. |
| Brazing | (english) Joining metals by fusion of nonferrous alloys that have melting points above 800 F (425C), but lower than those of the metals being joined. May be accomplished by a torch. Filler metal is ordinarily in rod form in torch brazing; whereas in furnace and dip brazing the work material is first assembled and the filler metal may then be applied as wire, washers, clips, bands, or may be bonded, as in brazing sheet. |
| Breakout | (english) An accident caused by the failure of the walls of the hearth of the furnace resulting in liquid iron or slag (or both) flowing uncontrolled out of the blast furnace. |
| Bridling | (english) The cold working of dead soft annealed strip metal immediately prior to a forming, bending, or drawing operation. A process designed to prevent the formulation of Luder's lines. Caution-Bridled metal should be used promptly and not permitted to (of itself) return to its pre-bridled condition. |
| Bright Annealed Wire | (english) Steel wire bright drawn and annealed in controlled non-oxidizing atmosphere so that surface oxidation is reduced to a minimum and the surface remains relatively bright. |
| Bright Annealing | (english) A process carried out usually in a controlled furnace atmosphere, so surface does not oxidize, remaining bright. |