| ใบอนุญาตเป็นผู้ประกอบวิชาชีพวิศวกรรมควบคุม | Licence for Professional Practice (วสท.) - or Controlled Engineer License , Registed Engineer License |
| Bainite | (english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite. |
| Bake | (english) Heat in an oven to a low controlled temperature to remove gases or to harden a binder. |
| Bake Hardenable Steel | (english) A cold-rolled, low-carbon sheet steel used for automotive body panel applications. Because of the steel’s special processing, it has good stamping and strength characteristics and after paint is baked on, improved dent resistance. |
| Baked Strength | (english) Compressive, shear, tensile or transverse strength of a mold sand mixture when baked at a temperature above 231 B0F (111 B0C) and then cooled to room temperature. |
| Balanced Steel | (english) Steels in which the deoxidisation is controlled to produce an intermediate structure between a rimmed and killed steel, Sometimes referred to as semi-killed steels, they possess uniform properties throughout the ingot and amongst their applications are boiler plate and structural sections. |
| Band Saw Steel (Wood) | (english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45. |
| Bars | (english) A relatively long straight, rigid piece pf metal; long steel products rolled from billets into such shapes as squares,rectangles, rounds,angles,channels,hexagons,and tees. In steel, “merchant bars” include rounds,flats,angles,squares,and channels that are used by fabricators to manufacture a wide variety of products such as furniture,stair railings and farm equipment. Concrete reinforcing bar (rebar) is used to strengthen concrete in highways,bridges and buildings. |
| Batch Anneal | (english) The process by which a large, stationary stack of steel coils (4 coils high) is subjected to a long heat-treating cycle. This process enables the cold-rolled sheet to fully recrystallize into the softest possible product conforming to customer specifications. Controlling the recrystallization process makes a fine-grained microstructure easy to obtain, and minimizes the tendencies for retention of directional properties of the rolled steel which could produce undesirable shapes in the stamping of a cylindrical part such as a can. Also see Anneal and Continuous Anneal. |
| Bend Test | (english) Various tests which is used to ascertain the toughness and ductility of a metal product, in which the material is bent around its axis and/ or around an outside radius. A complete test might specify such a bend to be both with and against the direction of grain. For testing, samples should be edge filed to remove burrs and any edgewise cracks resulting from slitting or shearing. If a vice is to be employed, then you must line the jaws with some soft metal, to permit a flow of the metal in the piece being tested. |