| Break Test (for tempered steel) | (english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges. |
| Breakage | (english) Cracks or separation of the steel. |
| Breaker | (english) Uncoiler rolls through which the strip passes; composed of a mandrel and leveling rolls which unwind the strip prior to processing through the Pickler. Breaker rolls assist in breaking up the Hot Mill surface scale. |
| Breakout | (english) An accident caused by the failure of the walls of the hearth of the furnace resulting in liquid iron or slag (or both) flowing uncontrolled out of the blast furnace. |
| Bridling | (english) The cold working of dead soft annealed strip metal immediately prior to a forming, bending, or drawing operation. A process designed to prevent the formulation of Luder's lines. Caution-Bridled metal should be used promptly and not permitted to (of itself) return to its pre-bridled condition. |
| Brinell Hardness Number | (english) The value of hardness of a metal on an arbitrary scale representing kg/mm2, determined by measuring the diameter of the impression made by a ball of given diameter applied under a known load. Values are expressed in Brinell Hardness Numbers, BHN |
| Brinell Hardness Testing | (english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function. |
| Brown Sharp Gages | (english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard. |
| Bruise | (english) A mark transferred to the strip surface from a defective process roll. Similar to dent or punchmark. |
| Buckles | (english) Appeaars like a series of waves and are created during rolling as a result of mechanical misalignment or cross-section irregularities in supply coil. |