| Brinell Hardness Number | (english) The value of hardness of a metal on an arbitrary scale representing kg/mm2, determined by measuring the diameter of the impression made by a ball of given diameter applied under a known load. Values are expressed in Brinell Hardness Numbers, BHN |
| Brinell Hardness Test | (english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula. |
| Brinell Hardness Testing | (english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function. |
| Brown Sharp Gages | (english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard. |
| Z-Mill | (english) The full name for z-mill is Sendzimir mill. A Z-mill operates with a very small diameter work roll, normally about 2 inches, backed up by a number of rolls in a pyramid-shaped stack. This roll set up allows you to exert extremely high forces through the work roll and yet keep the work roll from extreme flexing. The take-up roll on the Z-Mill also exerts a tension on the coil as it comes through the mill. The combination of high pressure and tension makes the mill capable of rolling material thin and flat. |
| Blaine Fineness | (Concrete Engineering) The fineness of granular materials such as cement and pozzolan, expressed as total surface area in square centimeters per gram, determined by the Blaine air-permeability apparatus and procedure. |
| Dry Rodded Weight | (Concrete Engineering) The weight of dry aggregate rodded into a cylindrical container of diameter approximately equal to the height, each of 3 layers rodded 25 times, and the excess aggregate struck off level with the top of the container |
| Mixing Speed | (Concrete Engineering) Rate of mixer drum rotation or that of the paddles in a pan, open-top, or trough type mixer, when mixing a batch; expressed in revolutions per minute (rpm) or in peripheral] feet per minute of A point on the circumference at maximum diameter. |
| Rod (tamping) (ASTM C24l) | (Concrete Engineering) A round, straight steel rod, 5/8' in diameter and approximately 24' in length, having the tamping end rounded into a hemispherical tip, the diameter of which is 5/8'. |
| Slump Cone | (Concrete Engineering) A metal mold in the form of a truncated cone with a top diameter of 4”, a bottom diameter of 8”, and a height of 12”, used to fabricate the specimen for a slump test. |